Glass fibers coated with composition adhesive to rubber

ABSTRACT

An aqueous alkaline dispersion of a rubbery vinyl pyridine copolymer, trimethylol phenol, and a resorcinol compound, in certain amounts, is useful in forming an adhesive for bonding glass fiber reinforcing elements or cords to rubber compounds or stocks. After dipping the glass fiber cord in the one-step adhesive dip, the coated cord is heated to dry it and heat cure or heat set the adhesive on the cord. Thereafter, the adhesive containing glass fiber cord is combined or laminated (calendered) with a curable rubber compound and the resulting assembly is cured to form a composite in which the glass fiber cord is bonded to the rubber by means of said adhesive.

This is a division, of application Ser. No. 380,939 filed July 19, 1973, and now U.S. Pat. No. 3,930,095.

OBJECTS

An object of the invention is to provide a composite of a glass fiber reinforcing element adhesively bonded to a rubber compound, e.g., glass fiber tire cords adhesively bonded to provide carcass plies and belt plies for making tires. Another object is to provide glass fiber reinforcing elements, e.g., such as those used in the belt and the carcass plies of tires, with a minor amount of an adhesive so that the adhesive containing elements may subsequently be bonded to rubber on curing. A further object is to provide a method for bonding glass fibers, particularly glass fiber textiles, fibers, cords and so forth, to rubber compounds using a single dip. These and other objects and advantages of the present invention will become more apparent to those skilled in the art from the following detailed description and working examples.

SUMMARY OF THE INVENTION

According to the present invention it has been discovered that a composition comprising essentially an aqueous alkaline dispersion generally of 100 parts by weight (dry) of a rubbery vinyl pyridine copolymer, from about 2 to 28 parts by weight of trimethylol phenol, from about 0.0 to 24 parts by weight of a water soluble resorcinol compound selected from the group consisting of resorcinol or a resorcinol-formaldehyde non heat hardenable, water soluble and thermoplastic compound (a fusible novolak or novolak resin), from about 0 to 3 parts by weight of an alkaline material selected from the group consisting of NH₄ OH and NaOH, and from about 170 to 1100 parts by weight of water, is very useful as a treating, dipping or coating material for use in bonding glass fiber reinforcing elements to rubber compounds. Sufficient alkaline material such as aqueous NH₃ or NaOH is added to the dispersion (or to one or more of the ingredients of the dispersion before mixing them together) to obtain the desired pH, prevent coagulation of the latex and to provide for stabilization. This will vary with the acidity of the resorcinol or novolak and the pH of the latex, all of which may vary from batch to batch. Since the amount of each compound may vary, the amount of alkaline material required can also vary. After drying the adhesive on the glass fiber reinforcing element to remove water and to heat cure or heat set the adhesive on the element, the adhesive containing elememt can then be combined or calendered with a curable rubber compound and the resulting assembly cured, usually in a mold, to provide a laminate exhibiting good adhesive properties.

The present method involves only one dipping step and the process or method can be varied to provide the desired pick-up or solids on the cord by varying the concentration of the dip or the speed of the cord through the dip to give the amount needed to develop the requisite adhesive bond. Thus, while the cord can be run through successive dips of the same or varying amounts of the above materials to get the desired buildup, this is unnecessary as satisfactory results can be accomplished in one dip. Pre or post dips of other adhesive compositions are unnecessary when using the present aqueous adhesive dip.

Another advantage in employing the glass fiber cord dip of the present invention is that the components of the dip do not need to be pre-reacted. Many of the dips are stable at high solids concentrations for extended periods of time. In many instances equivalent adhesion is observed at lower levels by weight of deposited dip solids. The dried and/or cured adhesive coated cord can exhibit higher tensile strengths, and the dried and/or cured adhesive coated cord can be coated uniformly without blister, in other words, it is smooth.

DISCUSSION OF DETAILS AND PREFERRED EMBODIMENTS

The glass fiber reinforcing element or cord comprises a plurality of substantially continuous and parallel glass fibers or monofilaments. The reinforcing element or fibers contain little or no twist. In other words, twist is not intentionally applied to the element or fibers; the only twist, if any, in the element or fibers is that occassioned on passing through the glass fiber processing apparatus and on packaging or winding up the cord to form a bobbin or spool. However, in a continuous process, the elements can proceed directly from the glass processing apparatus, can be dipped in the aqueous adhesive cord dip, dried, and given a twist of about 1.5 turns per inch thereafter. The elements then are woven into tire fabric having about one quite small pick thread or element, nylon or polyester, which may be a monofilament, per inch and calendered with a rubber ply or skim stock. The glass fiber reinforced ply stock is then ready to be used in the manufacture of a tire or for other purposes.

Glass compositions useful in making the fibers for the reinforcing element or glass tire cord are well known to the art. A preferred glass to use is a glass known as E glass and described in "Mechanics of Pneumatic Tires," Clark, National Bureau of Standards Monograph 122, U.S. Dept. of Commerce, issued November, 1971, pages 241-243, 290, and 291. The number of glass filaments or fibers employed in the glass fiber reinforcing element or cord can vary considerably depending on the ultimate use or service requirements. Likewise, the number of strands of glass fibers used to make a glass fiber reinforcing element or cord can vary widely. In general, the number of filaments in the glass fiber reinforcing element or cord for a passenger car tire can vary from about 500 to 3,000 and the number of strands in the reinforcing element can vary from 1 to 10, preferably the number of strands is from 1 to 7 and the total number of filaments about 2000. A representative industry tire cord known as G-75 has 5 strands each with 408 glass filaments. Another representative cord known as G-15 has a single strand containing 2040 glass filaments. In this connection reference is made to Wolf, "Rubber Journal," February, 1971, pages 26 and 27 and U.S. Pat. No. 3,433,689.

Shortly after the glass fibers are formed they are usually sized (by spraying or dipping and so forth and air drying) with a very small amount or fractional amount by weight of a material which acts as a protective coating during processing and handling of the glass fibers in forming the strands or reinforcing elements and during packaging. During the subsequent dipping in the aqueous adhesive tire cord dip, it is believed that the size is not removed. Materials for use as sizes for glass fibers are well known to the art. It is preferred to use a silane as a size, especially a silane which has groups which can bond or coordinate chemically or physically with at least parts of the surface of the glass of the glass fiber and with at least one or more of the components of the glass fiber aqueous adhesive cord dip. A very useful size to employ on the glass fibers is gammaaminopropyl triethoxy silane, or similar aminoalkyl alkoxy silanes, which, when applied to the glass fibers, hydrolyzes and polymerizes to form a poly(aminosiloxane) in which a portion of the polymer is attached to the glass and another portion contains amine groups (having active hydrogen atoms) for reaction with components of the cord dip such as the RF resin or the trimethylol phenol. Various glass fiber sizing compounds and compositions are shown in U.S. Pat. Nos. 3,252,278; 3,287,204; and 3,538,974.

The type of rubber latex used in the tire cord dip bath of this invention is a latex of a copolymer of a vinyl pyridine and a conjugated diolefin having 4 to 6 carbon atoms. The rubber latex is of the type described in U.S. Pat. No. 2,561,215 and comprises an aqueous dispersion of a copolymer of 50 to 95 percent by weight of a conjugated diolefin having 4 to 6 carbon atoms, 5 to 40 percent of a vinyl pyridine and 0 to 40 percent of a styrene. Examples of suitable vinyl pyridines are 2-vinyl pyridine, 4-vinyl pyridine, 2-methyl-5-vinyl pyridine, and 5-ethyl-2-vinyl pyridine.

In practicing this invention, it is usually preferred to use a latex of a copolymer of from about 60 to 80% by weight butadiene-1,3, about 7 to 32% styrene and about 5 to 22% of 2-vinyl pyridine. Excellent results are obtained using a latex of a terpolymer of about 70% by weight of butadiene-1,3, 15% styrene and 15% 2-vinyl pyridine having a total solids contents of around 30 to 50% by weight. Also, blends of latices may be used such as a blend of a butadiene-1,3/2-vinyl pyridine rubbery copolymer latex and a butadiene-1,3/styrene rubbery copolymer latex or a blend of a butadiene-1,3/styrene/2-vinyl pyridine rubbery copolymer latex and a butadiene-1,3/styrene rubbery copolymer latex so long as the percent by weight ratio of total monomers in the copolymers is within the ranges as specified above. The pH of the latices should be similar and the surfactants and stabilizers including freeze stabilizers should be compatible to avoid coagulation on blending or mixing of the latices. The polymers from these latices have Mooney viscosities ML-4 min. at 212°F. of from about 40 to 120. Further disclosures of rubbery vinyl pyridine copolymer latices may be found in U.S. Pat. Nos. 2,615,826 and 3,437,122.

The trimethylol phenol is prepared by the reaction of an excess of formaldehyde with phenol using a catalytic amount of base (NaOH) under nitrogen. The excess of H₂ CO drives the reaction to a high content of trimethylol phenol (2,4,6-trimethylol phenol) which is water soluble. The unreacted aldehyde can be removed by venting with reduced pressure. The base can be neutralized with acid to a pH of about 7. In preparing trimethylol phenol, after the first mol of formaldehyde has added to the phenol, the second and third additions are easier.

The resorcinol compound is resorcinol or a water soluble, thermoplastic and non-heat hardenable (without a curing agent or crosslinker) resorcinol-formaldehyde novolak or novolak resin or mixture thereof. The novolaks are prepared under acid conditions by the reaction of resorcinol and formaldehyde (or a formaldehyde donor like paraformaldehyde) to provide compounds having reactive phenolic hydroxy groups rather than methylol groups. The mol ratio of resorcinol to formaldehyde can vary over a considerable range to provide novolaks useful in the practice of the present invention although a preferred mol ratio of resorcinol to formaldehyde is about 1:0.5 to 2.0. These compounds and methods for making them are well known in the art.

Examples of commercially available resorcinol compounds are the water soluble novolak resins known as Arofene 779 (Ashland Chemical Co.) having a mol ratio of resorcinol to formaldehyde of about 1/0.62 and a commercially available novolak resin which comprises a mixture of about 15 parts by weight of resorcinol, 42.5 parts of diresorcinol methane (R/F/R) and 42.5 parts of a low molecular weight R/F novolak resin of a R/F mol ratio of about 3/2.

Since the resorcinol compound is acidic or prepared under acidic conditions, it should be neutralized or sufficient base such as NH₄ OH or NaOH added to it to prevent coagulation of the latex when the resorcinol compound is mixed with the latex. NaOH is preferred for dip viscosity stability. Even though the latex is alkaline, sufficient additional base may still be necessary to prevent such coagulation or premature coagulation and the consequent inability to use the dip properly.

Information on the preparation of the novolaks will be found in "Encyclopedia of Chemical Technology," Kirk-Othmer, Volume 15, Second Edition, 1968, Interscience Publishers Division of John Wiley & Sons, Inc., New York, pages 176 to 208; "Technology of Adhesives," Delmonte, Reinhold Publishing Corp., New York, N.Y., 1947, pages 30 to 31; and "Formaldehyde," Walker, A.C.S. Monograph Series, Reinhold Publishing Corp., New York, N.Y., Third Edition, 1964, pages 336 to 339.

Water is used in an amount sufficient to provide for the desired dispersion of the rubber or latex particles, for the solution of the trimethylol phenol and resorcinol compound, to obtain the desired viscosities, and for the proper solids content to get the necessary pick-up of solids on and penetration between the fibers of the cord.

Based on 100 parts by weight (dry weight) of the vinyl pyridine rubber copolymer, or blend of the same, the dip generally comprises the rubber, from about 2 to 28 parts by weight of the trimethylol phenol, from about 0.0 to 24 parts by weight of the resorcinol compound, from about 0 to 3.0 parts by weight of water soluble base such as NH₄ OH or NaOH to provide a pH of at least 7.0, and from about 170 to 1100 parts by weight of water.

In order to provide data for the tire cord adhesive of this invention, a standard single-cord H-pull test is employed to determine the static adhesion at room temperature and above of the adhesive-coated glass tire cord to rubber. All the data submitted herein including the working examples which follow are based upon identical test conditions, and all test specimens are prepared and tested in the same way generally in accordance with ASTM Designation: D 2138-67.

To apply the latex adhesive to the glass fiber cords in a reliable manner, the cords are fed through the adhesive dip bath while being maintained under a small predetermined tension and into a drying oven where they are dried under a small predetermined tension (to prevent sagging without any appreciable stretching). As the cords leave the oven they enter a cooling zone where they are air cooled before the tension is released. In each case the adhesive-coated cords leaving the dip are dried in the oven at from about 200° to 500°F. for from about 5-300 seconds, preferably at from about 400° to 450° F. for from about 90 to 30 seconds. The time the cord remains in the one-step adhesive dip is about a few seconds or so or at least for a period of time sufficient to allow wetting of the cord and at least substantial total impregnation of the fibers of the cord. The drying or curing of the adhesive treated glass fiber cord may be accomplished in one or more ovens at different times and temperatures.

The single-cord H-pull test is then employed to determine the static adhesion of the dried adhesive coated glass fiber cords to rubber. In each case the rubber test specimens are made from the same standard tupe rubber composition using the following recipe:

    Material                Parts by Weight                                        ______________________________________                                         Natural rubber, No. 3 smoked sheet                                                                     50.                                                    Rubbery butadiene-1,3/styrene                                                                          50.                                                     copolymer, cold emulsion copolymerized,                                        SBR-1502, about 23 1/2% by weight                                              bound styrene, Mooney viscosity ML-4                                           min. at 212°F=46-58                                                    Activated zinc salt of pentachloro-                                                                    0.5                                                     thiophenol, Endor, duPont                                                     Carbon black, high abrasion furnace                                                                    35.                                                    Zinc oxide              3.                                                     Stearic acid            1.                                                     Alkyl aromatic polyindene resin,                                                                       2.                                                      reinforcing and processing aid,                                                Picco 100, Pennsylvania                                                        Industrial Chemical Corp.                                                     Mixture of mono-, di- and tri-                                                                         1.                                                      styrenated phenols, AgeRite                                                    Spar, R.T. Vanderbilt Co., Inc.,                                               antioxidant                                                                   Circosol 2XH, naphthenic type                                                                          7.                                                      oil, Sun Oil Co.                                                              Diphenyl guanidine      0.5                                                    Nobs No. 1, selected blend of 90%                                                                      0.9                                                     Nobs Special (N-oxydiethylene                                                  benzothiazole-2-sulfenamide)                                                   and 10% MBTS (benzothiazyl                                                     disulfide), American Cyanamide Co.                                            Crystex, insoluble sulfur, specially                                                                   3.25                                                    refined elementary sulfur in                                                   polymerized form, Stauffer                                                     Chemical Co.                                                                  ______________________________________                                    

In every case the cords to be tested are placed in parallel positions in a multiple-strand mold of the type described in the single-cord H-pull adhesion test ASTM designated D 2138-67, the mold is filled with unvulcanized rubber of the above composition, the cords being maintained under a tension of 50 grams each, and the rubber is cured 20 minutes at around 305°F. to the elastic state. Each rubber test specimen is 1/4 inch thick and has a 3/8 inch cord embedment.

After the rubber has been cured, the hot reticulate cured rubber piece is removed from the mold, cooled and H-test specimens are cut from said piece, each specimen consisting of a single cord encased in rubber and having each end embedded in the center of a rubber tab or embedment having a length of around 1 inch or so. The specimens are then aged at least 16 hours at room temperature. The force required to separate the cord from the rubber is then determined at room temperature or 250°F. using an INSTRON tester provided with specimen grips. The maximum force in pounds required to separate the cord from the rubber is the H-adhesion value.

Cords or fabric coated with the adhesive of the present invention using the one-step or single dip of this invention can have from about 10 to 40% by weight (dry) solids of the adhesive dip on the cord based on the weight of the cord and can be used in the manufacture of carcasses, belts, flippers and chafers of radial, bias, or belted-bias passenger tires, truck tires, motorcycle and bicycle tires, off-the-road tires and airplane tires, and, also, in making transmission belts, v-belts, conveyor belts, hose, gaskets, rubbers, tarpaulins and the like.

The following examples will serve to illustrate the invention with more particularity to those skilled in the art. In these examples the parts are parts by weight unless otherwise indicated.

EXAMPLE I

The dip consisted of 100 grams vinyl pyridine rubber latex (1) to which 15 grams of 30% aqueous BRL-1031 (2) was added and subsequently a mixture of 5 grams of 50% aqueous Penacolite R-2170 (3) and 1 ml 2N aqueous NaOH. Fiberglass cords (4) were passed through the dip and then into an eight foot long tube in which hot air was blown in a direction opposite to the movement of the cord. The temperature where the air entered the tube was 60° to 90°F. higher than the temperature at the exit end of the tube. In Table I are recorded the highest temperatures during the drying or curing of the dipped cord. The speed of the cord through the oven can also be varied. After said drying and curing, the adhesive treated cords were laminated with the standard type rubber stock described supra, and molded, and the resulting assembly was cured for 20 minutes at 305°F. After curing, the assembly was removed from the mold, cooled and tested according to the H-adhesion test described supra. The following H-adhesions were obtained for the cords treated as described above.

                  Table I                                                          ______________________________________                                         H-Adhesion* of Glass Fiber Cord for Different                                  Processing Conditions                                                                      Time in oven (seconds)                                             Oven Temperature, °F                                                                  90       60       30     15                                      ______________________________________                                         400           36.1     35.1     35.4   29.3                                    425           32.8     36.3     32.2   28.5                                    450           34.1     33.1     34.1   27.5                                    475           19.6     28.0     33.2   27.6                                    ______________________________________                                          *3/8" embedment. H-adhesion in lbs. at RT, room temperature (about 22-         28°C.)                                                            

The results obtained show that better H-adhesions are obtained with curing accomplished at a temperature of from about 400° to 450°F. for from about 30 to 90 seconds.

Notes:

1. Aqueous alkaline (about pH 10.5 - 10.7) dispersion of a rubbery terpolymer of 70 parts by weight of butadiene-1,3, 15 parts of styrene and 15 parts of 2-vinyl pyridine, 41% by weight total solids (about 39% by weight rubber solids, balance surfactant, stabilizer) Mooney viscosity ML-4 min. at 212°F.= about 40, emulsion polymerized, freeze stable

2. Trimethylol phenol, Union Carbide Corp.

3. Preformed water-soluble resorcinol-formaldehyde novolak resin, Koppers Co., Inc.

4. G-15 cord, E glass, single strand tire cord of 2040 glass filaments, Owens-Corning Fiberglas Corporation.

EXAMPLE II

The method of this example was the same as that of Example I, above, except that all glass fiber cords were dried/cured for 60 seconds at 425°F. (maximum). Also, in A the dip is the same as the dip of Example I, above; in B the dip is the same as A except 25% by weight of the latex has been replaced with SBR-2000 (5); in C the dip is the same as A except that 50% by weight of the latex has been replaced with SBR-2000; and in D a commercially available dipped G-15 glass fiber tire cord (6) was tested. The results of the tests are shown in Table II, below:

                  Table II                                                         ______________________________________                                                            Tensile Strength                                                                             H-Adhesion                                    Viscosity  Pickup  of Dipped Cord                                                                               lbs.                                          Run  cp (7)    % (8)   lbs. (9)    RT   250°F                           ______________________________________                                         A    20.5      23.0    63.8        33   21                                     B    15.5      21.6    72.7        34   22                                     C    58.0      21.1    68.6        32   21                                     D    --        28.6    60.4        33   22                                     H-Adhesion, lbs., RT                                                           In Rubber Aging                                                                24 hrs., 300°F                                                                               Peel Test (12) lbs.,                                      Run  dry (10)  over water (11)                                                                              RT     250°F                               ______________________________________                                         A    28        22            45     31                                         B    29        22            47     30                                         C    30        24            36     25                                         D    32        21            45     23                                         ______________________________________                                    

The results of these tests show that blends of latices can be used with achievement of comparable results. The cords of the present invention using blended latices also show increased tensile strengths.

Notes:

5. Emulsion polymerized copolymer of butadiene1,3 and styrene, about 47% by weight of bound styrene, Mooney viscosity ML-4 min. at 212°F.= about 77, about 42% total solids, not polymerized, pH about 11.2.

6. Dipped G-15 glass fiber cord. Corp dip composition on cord was unknown. Owens-Corning Fiberglas Corp.

7. Centipoises, viscosity determined after 21 days; initial viscosity was 12.5 cp.

8. By weight. Pickup determined by ignition loss.

9. Test used was ASTM D2970.

10. sample was heated in a closed container at 300°F. for 24 hours under nitrogen before conducting H-adhesion test.

11. Sample was heated in a closed container with water present at 300°F. for 24 hours under nitrogen before conducting H-adhesion test.

12. Test used was modified ASTM D2630. Crosshead speed was 2 inches per minute.

EXAMPLE III

The method of this Example was the same as that of Examples I and II above, except that the ratio of the trimethylol phenol to the novolak as well as their total amounts were varied. The dipped cords were cured at 425°F. for 45 seconds, and the latex used was a mixture of 75 parts by weight of the above vinyl pyridine latex and 25 parts by weight of the SBR-2000 latex. The results obtained are summarized in Table III, below:

                  Table III                                                        ______________________________________                                               Total dry weight                                                               (2)+(3)         Dry                                                            per 100         Weight                                                   Run   Parts by weight of                                                                             ratio     Viscosity, cp                                  No.   dry rubber (Phr) blend                                                                         (2)/(3)   after 3 months                                 ______________________________________                                         1     34              0.90      coag.*after 3 mos.                             2     34              1.39      coag.*after 1 mo.                              3     34              1.84      coag. in 4 days                                4     17              0.90      17.0                                           5     17              1.39      12.6                                           6     17              1.84      14.5                                           7     8.5             0.90      14                                             8     8.5             1.39      14                                             9     8.5             1.84      14                                             10    5.0             0.90      14.5                                           11    5.0             1.39      15.5                                           12    5.0             1.84      16.0                                                 Dried                                                                    Run   Dipped cord % Ignition H-Adhesion, lbs.                                  No.   Tensile, lbs.                                                                              Loss, by wt.                                                                              RT     250°F                               ______________________________________                                         1     65.6        19.4       35.7   20.8                                       2     60.5        20.6       37.6   22.4                                       3     --          --         --     --                                         4     65.1        19.1       32.2   21.6                                       5     63.3        18.4       34.5   24.5                                       6     71.6        16.2       34.0   22.6                                       7     67.8        14.7       33.4   21.4                                       8     65.0        12.7       31.4   20.3                                       9     68.3        11.4       28.6   21.1                                       10    63.6        14.3       31.3   21.1                                       11    66.4        14.5       31.9   20.4                                       12    67.3        14.5       32.1   20.3                                       ______________________________________                                          *coag -- Dip coagulated                                                  

The results of these tests show that considerable variation can be made in the components of the dip with obtainment of useful adhesions for the rubber stock to the glass fiber cord. The dips of Runs 7-9 are viscosity stable for about three months.

EXAMPLE IV

The method of this Example was the same as that of Example III, above, except that the foregoing Runs Nos. 4, 5 and 6 were tested more extensively. The results obtained are compiled in Table IV, below:

                  Table IV                                                         ______________________________________                                         Run   Dry Weight Ratio                                                                             Peel Test, lbs.                                            No.   (2)/(3)       RT           250°F                                  ______________________________________                                         4-IV  0.90          29.9         15.7                                          5-IV  1.39          29.2         21.5                                          6-IV  1.84          32.0         25.4                                          Run   H-adhesion, After in Rubber Aging, lbs., RT                              No.   N.sub.2, 300°F 24 hrs.                                                                 N.sub.2 + H.sub.2 O, 300°F 24                      ______________________________________                                                              hrs.                                                      4-IV  29.2           20.6                                                      5-IV  26.2           22.6                                                      6-IV  26.8           20.7                                                      ______________________________________                                    

EXAMPLE V

The method of this Example was the same as that of Example IV, above, except that the amount of aqueous NaOH was reduced so that it was used in an amount just enough to neutralize the Penacolite R-2170. The results obtained after testing are shown in Table V, below:

                  Table V                                                          ______________________________________                                         Run   Dry Weight Ratio                                                                             Peel Test, lbs.                                            No.   (2)/(3)       RT           250°F                                  ______________________________________                                         4-V   0.90          35.6         23.7                                          5-V   1.39          49.2         30.2                                          6-V   1.85          48.9         30.9                                          Run   H-Adhesion, lbs.                                                         No.   RT       250°F                                                    ______________________________________                                         4-V   33.7     22.4                                                            5-V   36.7     24.8                                                            6-V   33.4     23.6                                                            ______________________________________                                    

The dips of these runs are viscosity stable for about a month.

EXAMPLE VI

The method of this Example, was the same as that of Example V, above, except that the total amount of the BRL-1031 and of the novolak was reduced. The results on testing are shown in Table VI, below:

                  Table VI                                                         ______________________________________                                         Change of Viscosity of Dips With Time                                          Resin content phr (dry), By weight                                             BRL-1031        Penacolite R-2170                                              ______________________________________                                         A     6.5           6.0                                                        B     7.5           5.0                                                        C     8.4           4.0                                                        D      9.45         3.0                                                        Viscosity, cp after:                                                                 1 day    10 days    21 days  30 days                                     ______________________________________                                         A     10.0     10.0       10.5     11.5                                        B     10.0     11.5       11.5     11.5                                        C     11.0     12.0       12.0     12.0                                        D     11.5     12.0       12.0     12.0                                        ______________________________________                                    

The average H-adhesion on glass of these four dips after 30 days was around 31 lbs. when pulled at room temperature and 16-18 lbs. when pulled at 250°F. These dips, also, are stable for at least 30 days.

EXAMPLE VII

The method of this Example was the same as that of Example VI, above, except that after 11 days different amounts of neutralized Penacolite R-2170 were added to the latex/BRL-1031 dispersion. These mixtures (TS = 40%) were used for the G-15 glass fiber cord. The processing conditions and laminating rubber stock are those already mentioned above.

                  Table VII                                                        ______________________________________                                         Delayed Addition of Penacolite R-2170                                          Adhesions on Glass                                                             Resin, phr (dry), by weight                                                                       H-Adhesions, lbs.                                           BRL-1031                                                                               Penacolite R-2170                                                                             RT        250°F                                  ______________________________________                                          9.6    7.5            29.8      18.6                                          12.6    7.5            30.8      19.0                                          15.9    7.5            31.1      18.6                                          18.9    7.5            31.8      20.2                                          14.4    10.0           30.7      19.2                                          17.1    13.6           30.6      19.6                                          ______________________________________                                    

EXAMPLE VIII

The method of this Example was the same as that of Example VII, above, except that the dip (40% total solids) contained 15 parts (dry) per hundred of the rubber blend (dry) of the BRL-1031 and 1.25 phr of the Penacolite R-2170. The dips were aged before the glass cords were dipped in them. The results on testing are shown in Table VIII, below:

                  Table VIII                                                       ______________________________________                                         Dip Aging Treatment                                                                            H-Adhesion, lbs., RT                                           ______________________________________                                         5 days at RT    30                                                             6 days at RT    30                                                             2 hrs. at 50°C.                                                         then 5 days at RT                                                                              30                                                             ______________________________________                                    

No measurable viscosity increase after heat treatment.

EXAMPLE IX

The method of this Example was the same as that for Example VIII, above, except that two levels of Penacolite or of resorcinol were used and the dips were heated for 4 hours at 50°C. (with no measurable viscosity increase) before the glass fiber cords were dipped in them. The results obtained on test are shown below in Table IX:

                  Table IX                                                         ______________________________________                                         Resin Component   H-Adhesion, lbs., RT                                         ______________________________________                                         Penacolite R-2170, 1.25 phr                                                                      32                                                           Penacolite R-2170, 1.56 phr                                                                      32                                                           Resorcinol, 1.25 phr                                                                             32                                                           Resorcinol, 1.56 phr                                                                             33                                                           ______________________________________                                    

While in the foregoing examples, the adhesive containing glass fiber reinforcing elements can be adhered to a vulcanizable blend of natural rubber and rubbery butadiene-styrene copolymer by curing the same in combination together, it is apparent that said heat cured adhesive containing glass fiber reinforcing element can be adhered to other vulcanizable rubbery materials, by curing or vulcanizing the same in combination with the rubber, such as one of the foregoing rubbers as well as nitrile rubbers, chloroprene rubbers, polyisoprenes, polybutadienes, vinyl pyridine rubbers, acrylic rubbers, isoprene-acrylonitrile rubbers and the like and mixtures of the same. These rubbers can be mixed with the usual compounding ingredients including sulfur, stearic acid, zinc oxide, magnesium oxide, accelerators, antioxidants and other curatives, rubber compounding ingredients and the like well known to those skilled in the art for the particular rubbers being employed. 

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:
 1. A glass fiber reinforcing element containing from about 10 to 40% by weight (dry) based on the weight of said element of a heat cured adhesive composition useful for adhering said element to a rubber compound and comprising essentially 100 parts by weight of a rubbery vinyl pyridine copolymer, from about 2 to 28 parts by weight of trimethylol phenol and from about 1.25 to 24 parts by weight of at least one water soluble, thermoplastic and non heat hardenable resorcinol compound selected from the group consisting of resorcinol and a resorcinol-formaldehyde novolak, said composition coating and at least substantially totally impregnating said element.
 2. A glass fiber reinforcing element containing from about 10 to 40% by weight (dry) based on the weight of said element of a heat cured adhesive composition useful for adhering said element to a rubber compound and comprising essentially 100 parts by weight of a rubbery vinyl pyridine copolymer, from about 2.4 to 22.1 parts by weight of trimethylol phenol and from about 1.25 to 17.9 parts by weight of at least one water soluble, thermoplastic and non heat hardenable resorcinol compound selected from the group consisting of resorcinol and a resorcinol-formaldehyde novolak, said composition coating and at least substantially totally impregnating said element.
 3. A glass fiber reinforcing element according to claim 2 in which said non-heat hardenable resorcinol compound is resorcinol.
 4. A glass fiber reinforcing element according to claim 2 in which said non-heat hardenable resorcinol compound is a resorcinol-formaldehyde novolak.
 5. A glass fiber reinforcing element according to claim 2 wherein said rubbery vinyl pyridine copolymer is a copolymer of from about 60 to 80% by weight of butadiene 1,3, from about 7 to 32% by weight of styrene, and from about 5 to 22% by weight of 2-vinyl pyridine and where said resorcinol compound is made by reacting resorcinol with formaldehyde in the mol ratio of about 1:0.5 to
 2. 6. A glass fiber reinforcing element according to claim 5 where said element is a cord of about 2040 substantially parallel and continuous E glass filaments.
 7. A glass fiber reinforcing element according to claim 5 where said rubbery vinyl pyridine copolymer is a terpolymer of about 70% by weight of butadiene-1,3, 15% of styrene and 15% of 2-vinyl pyridine.
 8. A glass fiber reinforcing element according to claim 5 where said copolymer is a blend of a terpolymer of butadiene-1,3, styrene and 2-vinyl pyridine and a copolymer of butadiene-1,3 and styrene.
 9. A glass fiber reinforcing element according to claim 8 where said terpolymer is present in an amount of 75% by weight and said copolymer is present in an amount of 25% by weight.
 10. A glass fiber reinforcing element according to claim 8 where said terpolymer is present in an amount of 50% by weight and said copolymer is present in an amount of 50% by weight. 